Antero 800NA is a PEEK-based FDM thermoplastic. It combines FDM's design freedom and ease of use with excellent strenght, toughness and wear-resistant properties of PEEK material. Antero 800NA exhibits high resistance, chemical resistance, low outgassing and dimensional stability, particularly in large parts.

Appropriate applications include aircraft components exposed to jet fuel, oil and hydraulic fluid, spacecraft parts that demand low outgassing and chemical-resistant industrial parts. Using Antero 800NA with FDM technology avoids the waste associated with subtractive manufacturing of high-cost bulk PEEK material.

Mechanical Properties Test Method XZ AXIS ZX AXIS
Tensile Strength, Ultimate (Type 1, 0.125 in., 0.2 in./min) ASTM D638 93.1 ± 0.4 MPa 45.9 ± 5.3 MPa
Tensile Modulus (Type 1, 0.125 in., 0.2 in./min) ASTM D638 3.1 ± 0.3 GPa 3.5 ± 0.7 GPa
Elongation at break (Type 1, 0.125 in., 0.2 in./min) ASTM D638 6.40 ± 1.05% 1.22 ± 0.28 %
Flexural Strength (Method 1, 0.05 in./min) ASTM D790 142 ± 3 MPa 64 ± 10 MPa
Flexural Modulus (Method 1, 0.05 in./min) ASTM D790 3.1 ± 0.1 GPa 2.7 ± 0.1 GPa
Flexural Strain at Break (Method 1, 0.05 in./min) ASTM D790 No break 2.41 ± 0.39%
Notched Impact (Method A, 23°C) ASTM D256 37 ± 6 J/m 27 ± 5 J/m
Compressive Strenght Ultimate (Method 1, 0.05 in./min) ASTM D695 100 ± 2 MPa 101 ± 3 MPa
Compressive Modulus (Method 1, 0.05 in./min) ASTM D695 2.45 ± 0.01 GPa 2.3 ± 0.01 GPa
Thermal Properties Test Method VALUE  
Glass Transition temperature (Tg) ASTM D7426-08 149°C  
Heat Deflection (HDT) @ 66 psi ASTM D648 150°C  
Heat Deflection (HDT) @ 264 psi ASTM D648 147°C  
Electrical Properties Test Method XY (Value Range) ZX (Value Range)
Volume Resistivity ASTM D257 > 1.4 x 1014 ohm > 1.4 x 1014 ohm
Dielectric Constant ASTM D150-98 3.23 3.32
Dissipation Factor ASTM D150-98 0.004 0.003
Other Test Method Metric Available Colors
Specific Gravity ASTM D792 1.28
Natural
Chemical Compatibility MIL-STD-810G No visible damage