Nylon12 CF

Il Nylon 12CFTM è un materiale termoplastico caricato carbonio con eccellenti caratteristiche strutturali. Il materiale è composto da una miscela di nylon 12 e fibra di carbonio al 35%: questa combinazione produce uno dei materiali termoplastici più resistenti per la tecnologia FDM. Il Nylon 12CFTM è il materiale con la più alta resistenza a flessione tra i termoplastici FDM oltre a garantire il più alto rapporto rigidità / peso.
Le applicazioni riguardano parti robuste ma leggere e prototipi funzionali nei settori aerospaziale, automotive ed industriale.

Mechanical Properties1 Test Method XZ AXIS ZX AXIS
Tensile Strength (Type 1, 0.125”, 0.2”/min) PSI ASTM D638 63.4 MPa 28.8 MPa
Tensile Strength, Ultimate (Type 1, 0.125”, 0.2”/min) PSI ASTM D638 75.6 MPa 34.4 MPa
Tensile Modulus (Type 1, 0.125”, 0.2”/min) PSI ASTM D638 7515 MPa 2300 MPa
Elongation at Break (Type 1, 0.125”, 0.2”/min) % ASTM D638 1.9% 1.2%
Elongation at Yield (Type 1, 0.125”, 0.2”/min) % ASTM D638 0.9% 1.1%
Flexural Strength (Method 1, 0.05”/min) PSI ASTM D790 142 MPa 58.1 MPa
Flexural Modulus (Method 1, 0.05”/min) PSI ASTM D790 10,620 MPa 1,830 MPa
Flexural Strain at Break (Method 1, 0.05”/min) PSI ASTM D790 3% 3%
IZOD Impact, notched (Method A, 23°C) ft-lbf/in ASTM D256 85 J/m 21.4 J/m
IZOD Impact, un-notched (Method A, 23°C) ft-lbf/in ASTM D256 310 J/m 85 J/m
Thermal Properties2 Test Method Metric  
Heat Deflection (HDT) @ 66 psi ASTM D648 -  
Heat Deflection (HDT) @ 264 psi ASTM D648 143°C  
Vicat Softening Temperature (Rate B/50) ASTM D1525 -  
Glass Transition Temperature (Tg) DMA (SSYS) -  
Coefficient of Thermal Expansion (flow) ASTM E831 -  
Coefficient of Thermal Expansion (xflow) ASTM E831 -  
Melting Temperature - 223°C  
Electrical Properties Test Method Metric  
Volume Resistivity (kOhms) ASTM D257 5.4E+03 - 3.9E+04  
Surface Resistivity (kOhms) ASTM D257 3.3E+03 - 6.9E+04  
Dielectric Constant ASTM D150-98 -  
Dissipation Factor ASTM D150-98 -  
Dielectric Strength ASTM D149-09, Method A -  
Other Test Method Metric  
Specific Gravity) ASTM D792 1.15  
Flame Classification UL94 HB  
Rockwell Hardness ASTM D785 -  
UL File Number - E345258  
      Available Colors

The information presented are typical values intended for reference and comparison purposes only. They should not be used for design speci cations or quality control purposes. End-use material performance can be impacted (+/-) by, but not limited to, part design, end-use conditions, test conditions, etc. Actual values will vary with build conditions. Tested parts were built on Fortus 450mc @ 0.010” (0.254 mm) slice. Product speci cations are subject to change without notice.
The performance characteristics of these materials may vary according to application, operating conditions or end use. Each user is responsible for determining the Stratasys material is safe, lawful and technically suitable for the intended application, as well as for identifying the proper disposal (or recycling) method consistent with applicable environmental laws and regulations. Stratasys makes no warranties of any kind, express or implied, including, but not limited to, the warranties of merchantability, tness for a particular use or warranty against patent infringement.
1 Build orientation is on side long edge.
2 Literature value unless otherwise noted.