Nylon 6

[ DOWNLOAD PDF ] [ Altri Materiali ]
Nylon 6

Il Nylon 6TM combina resistenza e durezza superiori ad altri materiali termoplastici FDM per essere utilizzato nella costruzione di componenti o utensili robusti, personalizzati, di lunga durata e che resistono a rigorosi test funzionali

Il Nylon 6TM è perfetto per la produzione di parti durevoli, dall’ottima resa superficiale e con un’elevata resistenza a rottura. Il Nylon 6TM è l’ideale per progettisti ed ingegneri dei settori automobilistico, aerospaziale ed industriale.

[ QUOTA IL TUO MODELLO! ]
Mechanical Properties1 - Conditioned* Test Method XZ AXIS ZX AXIS
Tensile Strength (Type 1, 0.125”, 0.2”/min) ASTM D638 49.3 MPa 28.9 MPa
Tensile Strength, Ultimate (Type 1, 0.125”, 0.2”/min) ASTM D638 67.6 MPa 36.5 MPa
Tensile Modulus (Type 1, 0.125”, 0.2”/min) ASTM D638 2,232 MPa 1,817 MPa
Elongation at Break (Type 1, 0.125”, 0.2”/min) ASTM D638 30% 3.2%
Elongation at Yield (Type 1, 0.125”, 0.2”/min) ASTM D638 2.3% 1.7%
Flexural Strength (Method 1, 0.05”/min) ASTM D790 97.2 MPa 82 MPa
Flexural Modulus (Method 1, 0.05”/min) ASTM D790 2,196 MPa 1,879 MPa
Flexural Strain at Break ASTM D790 No Break No Break
IZOD Impact, notched (Method A, 23°C) ASTM D256 106 J/m 43 J/m
IZOD Impact, un-notched (Method A, 23°C) ASTM D256 2,873 J/m 192 J/m
Thermal Properties2 Test Method Metric  
Heat Deflection (HDT) @ 264 psi annealed - 93°C  
      Available Colors
     
Black

*Conditioned = 20°C and 50% RH for 40 hours
The information presented are typical values intended for reference and comparison purposes only. They should not be used for design speci cations or quality control purposes. End-use material performance can be impacted (+/-) by, but not limited to, part design, end-use conditions, test conditions, etc. Actual values will vary with build conditions. Tested parts were built on Fortus 400mc @ 0.010” (0.254 mm) slice. Product speci cations are subject to change without notice.

The performance characteristics of these materials may vary according to application, operating conditions, or end use. Each user is responsible for determining that the Stratasys material is safe, lawful, and technically suitable for the intended application, as well as for identifying the proper disposal (or recycling) method consistent with applicable environmental laws and regulations. Stratasys makes no warranties of any kind, express or implied, including, but not limited to, the warranties of merchantability, tness for a particular use, or warranty against patent infringement.

1Literature value unless otherwise noted.