| Mechanical Properties | Test Method | English | Metric |
| Tensile Strength | ASTM D638 | 6,237 psi | 43 MPa |
| Tensile Modulus | ASTM D638 | 230 ksi | 1,568 MPa |
| Elongation at Break | ASTM D638 | 14% | 14% |
| Flexural Strength | ASTM D790 | 6,962 psi | 48 MPa |
| Flexural Modulus | ASTM D790 | 201 ksi | 1,387 MPa |
| IZOD Impact, notched (Method A, 23°C) | ASTM D256 | 0.6 ft-lb/in | 32 J/m |
| IZOD Impact, un-notched (Method A, 23°C) | ASTM D256 | 6.3 ft-lb/in | 336 J/m |
| Gardner Impact | ASTM D5420 | 2.0 ft-lb | 2.7 J |
| Thermal Properties | Test Method | English | Metric |
| Heat Deflection (HDT) @ 66 psi | ASTM D648 | 356°F | 180°C |
| Heat Deflection (HDT) @ 264 psi | ASTM D648 | 203°F | 95°C |
| Coefficient Thermal Expansion 0-50 °C | ASTM E831 | 45.9 μin/in°F | 82.6 μm/m°C |
| Coefficient Thermal Expansion 85-145 °C | ASTM E831 | 99.6 μin/in°F | 179.2 μm/m°C |
| Other | Test Method | Value | Available Colors | |
| Shore Hardness (D) | D2240 | 73 |
|
|
| Water absorption, % - 24 hours | D570 | 0.07 % | ||
| Dielectric Strength | D149 | 17.3 kV/mm | ||
| Dielectric Constant @ 1 Khz | D150 | 2.73 | ||
| Dissipation Factor @ 1 Khz | D150 | 0.044 | ||
| Specific Gravity | ASTM D792 | 1.00g/cm3 |
The information presented are typical values intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes.
End-use material performance can be impacted (+/-) by, but not limited to, part design, end-use conditions, etc. Actual values will vary with build conditions.
Product specifications are subject to change without notice.
The performance characteristics of these materials may vary according to application, operating conditions, or end use. Each user is responsible for determining that the material is safe, lawful and technical suitable for the intended laws and regulations. Zare makes no warranties of any kind, express or implied, including, but not limited to, the warranties of merchantability, fitness for a particular use, or warranty against patent infringement.
All Trademarks included in this document are property of the respective owner